Damage Condition Possible Causes Countermeasures
Bearing rust and corrosion are pits on the surface of rings and rolling elements and may occur at the rolling element pitch on the rings or over the entire bearing surfaces.
  • Entry of corrosive gas or water
  • Improper lubricant
  • Formation of water droplets due to condensation of moisture
  • High temperature and high humidity while stationary
  • Poor rust-preventive treatment during transporting
  • Improper storage conditions
  • Improper handling
  • Improve the sealing mechanis
  • Study the lubrication method
  • Anti-rust treatment during periods of non-running
  • Improve the storage methods
  • Improve the handling method

 

Click a photo to enlarge it

Rust and Corrosion 1

Part: Outer ring of a cylindrical roller bearing
Symptom: Rust on the rib face and raceway surface
Cause: Water entry

Rust and Corrosion 2

Part: Outer ring of a slewing ring
Symptom: Rust on raceway surface at ball pitch intervals
Cause: Moisture condensation during stationary periods

Rust and Corrosion 3

Part: Inner ring of a spherical roller bearing
Symptom: Rust on raceway surface at roller pitch intervals
Cause: Entry of water into lubricant

Rust and Corrosion 4

Part: Rollers of a spherical roller bearing
Symptom: Pit-shaped rust on rolling contact surface. Corroded portions.
Cause: Moisture condensation during storage

Downloads

Contact Search

Please select your options to view your contact.

Your result

Cookies on the NSK website

We use cookies to ensure that we give you the best experience on our websites and web applications. By continuing without changing your browser settings, we assume you give your consent to receive cookies. However, you can change your browser cookie setting at any time.